電工鋼硅鋼片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Specific total loss (iron loss) is the total power consumed per unit mass of material when the magnetic polarization waveform remains sinusoidal, with a specific peak and frequency. The specific total loss is represented by the symbol P (Jm/f), in W/kg. Example: P1.5/50 represents the specific total loss at a maximum magnetic polarization intensity of 1.5T and a frequency of 50Hz. 3.2 Magnetic Polarization Q/BQB 480-20212 Magnetic polarization intensity refers to the peak magnetic polarization intensity of a specific magnetic field intensity when a sample is subjected to alternating magnetization. Its symbol is J (H), and the unit is T (Tesla). Example: J5000 represents the peak magnetic polarization intensity corresponding to a magnetic field intensity peak of 5000A/m. The material grades in this document are classified based on the nominal maximum specific total loss P1.5/50 (W/kg) at a magnetic polarization strength of 1.5T and a frequency of 50Hz, as well as the nominal thickness of the material. They are further divided into three categories based on product characteristics: ordinary type, stress relief annealing type, and high-efficiency type. Example 1: B35A210 represents a common non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 2.10W/kg； Example 2: B35AR300 represents a stress relieved annealed non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific total loss value P1.5/50 is 3.00W/kg； Example 3: B35AH230 represents an efficient non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. Example 4: 35WW210 represents a normal type WW non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.10W/kg. Example 5: 35WH230 represents an efficient WH non oriented electrical steel with a nominal thickness of 0.35mm, and the maximum nominal specific loss value P1.5/50 is 2.30W/kg. The classification and code of insulation coatings shall comply with the provisions of Table 2. Table 2 Classification and Code of Insulation Coatings Type Code Characteristics of Insulation Coatings Semi organic Thin Coating A Improves Punching Performance and Has Good Weldability Semi organic Thick Coating H has Good Punching Performance and High Interlayer Resistance Semi organic Chromium Free Thin Coating K does not contain chromium and has good weldability Semi organic Chromium Free Thick Coating M does not contain chromium and has good insulation performance Semi organic Chromium Free Extreme Thick Coating J does not contain chromium and has excellent insulation performance Semi organic Chromium Free Ultra Thick Coating L does not contain chromium and has extremely high insulation performance Self adhesive Coating

電工鋼硅鋼片：電工鋼鋼板經沖片、江蘇宿遷本地剪切、江蘇宿遷本地彎曲會引入殘余應力，導致磁性能劣化。應力退火（SRA）可以殘余應力對磁疇移動與轉動的阻礙作用，恢復電磁性能。E.2 在鋼板或疊鐵心的狀態(tài)下進行應力退火的注意事項如下。1). 避免氧化和滲碳為了防止氧化應力退火應該在保護氣氛下進行，通常是 10％以下氫氣（H2）和 90％以上氮氣（N2）、江蘇宿遷本地100％氮氣（N2）或者氨分解氣氛的非爆炸性保護氣氛，露點控制在 0℃以下。沖壓加工過程引入的沖壓油在退火前應完全去除，防止在退火中發(fā)生滲碳，劣化產品磁性。2). 退火溫度及保持時間退火溫度指材料溫度，750℃為宜。為使得鋼板各部分退火均勻，需要調整溫度與保持時間。溫度太低不足以殘余應力的影響，溫度太高會破壞涂層絕緣性。3). 冷卻時間應當避免急劇冷卻使材料產生應力應變。冷卻時間根據電工鋼退火數量進行調整。對于退火小噸位數量時，可按每小時不超過 25℃ 的冷卻速度冷卻到 350℃,以避免冷卻過程中產生應力應變。對于退火大噸位數量時，應采取更加緩慢的冷卻速率，以期獲得 效果。