二是要看蜂窩活性炭產(chǎn)品所產(chǎn)生的氣泡，如果產(chǎn)生的氣泡越多則產(chǎn)品的質(zhì)量就越好。我們可以做一個小實驗，將一小把蜂窩活性炭產(chǎn)品投入水中，由于水滲透的作用，水會隨之浸入活性炭的孔隙中，以此來讓孔隙中的空氣排出，從而產(chǎn)生一連串的極為小的氣泡，在水中拉出一條細小的氣泡線，同時又發(fā)出了茲茲的氣泡聲，看著十分有趣。如果這種現(xiàn)象發(fā)生的很劇烈的話，而且持續(xù)的時間越長，那么就證明蜂窩活性炭產(chǎn)品的孔隙結(jié)構非常發(fā)達，就是蜂窩活性炭的吸附性越好的表現(xiàn)。
  
  The two is to look at the honeycomb activated carbon products produced by the bubble, if the bubble is more the better the quality of the product. We can do a little experiment, a handful of honeycomb activated carbon products into the water, because the water penetration effect, water will be immersed in the pores of activated carbon, so the pore in the air, resulting in a series of very small bubbles, pulled out a tiny bubbles lines in the water, at the same time also issued Zizi bubble sound, looked very interesting. If this phenomenon is very serious, and the longer the duration, then it is proved that the honeycomb activated carbon product pore structure is very developed, that is, the better adsorption performance of honeycomb activated carbon.

蜂窩活性炭生產(chǎn)方法 步是：褐煤或煙煤與焦煤分別破碎到小于2毫米(mm)，然后按質(zhì)量比褐煤或煙煤∶焦煤為1∶0.2—0.5混合后，再研磨至74米(μm)以下，會得到混合均勻的煤粉。

  蜂窩活性炭生產(chǎn)方法第二步是：1、瀝青含量大于等于55%高溫煤焦油預熱至120—150℃;2、乳化劑水溶液的配制，在水中加入高溫煤焦油質(zhì)量的2—6%表面活性劑和高溫煤焦油質(zhì)量的0.5—2%的穩(wěn)定劑，并預熱至80—90攝氏度(℃)形成乳化劑水溶液，3、按質(zhì)量比為高溫煤焦油∶乳化劑水溶液=1∶0.3—0.7，在攪拌條件下，將高溫煤焦油加入乳化劑水溶液中制成乳化煤焦油。

  蜂窩活性炭生產(chǎn)方法第三步是：按質(zhì)量比為煤粉∶乳化煤焦油∶水∶水溶性粘合劑∶潤滑劑=34—57∶30—36∶6—29∶3—5∶2—3，將其加入捏合機當中攪拌均勻后，能夠制成可塑性的煤泥。

  蜂窩活性炭生產(chǎn)方法第四步是：可塑性煤泥經(jīng)過真空練泥機或擠出成型機處理，使得煤泥混合均勻，然后在成型機中用60—100目的絲網(wǎng)中過濾除掉大顆粒物質(zhì)。

  蜂窩活性炭生產(chǎn)方法第五步：練泥處理后的煤泥加入裝有蜂窩鋼模具的擠出成型機中，進行成型，得到濕的蜂窩體。

  蜂窩活性炭生產(chǎn)方法第六步：濕的蜂窩體干燥至水分低于2%;以惰性氣體作為保護氣，按升溫速度3-5℃/min(攝氏度/分鐘)加熱到600—800℃，并且在此溫度下炭化2—3個小時;然后按升溫速度5—15℃/min(攝氏度/分鐘)升溫到750—850℃，用水蒸氣活化3—15個小時，經(jīng)過多道工藝終于制成蜂窩活性炭。